Proses Fabrikasi Dan Pencirian Bahan Komposit Laminat Untuk Industri Kapal Terbang

Abdul Razak , Bahtrem (2007) Proses Fabrikasi Dan Pencirian Bahan Komposit Laminat Untuk Industri Kapal Terbang. Project Report. UTeM, Melaka. (Submitted)

[img]PDF (24 Pages) - Submitted Version
4Mb
[img]PDF (Full Text) - Submitted Version
Restricted to Registered users only

20Mb

Official URL: http://library.utem.edu.my:8000/elmu/index.jsp?mod...

Abstract

Laminate composite of CFRP were fabricated using hand lay up process at ± 45° orientation with 10 layers of plies. The laminates were autoclave cured at 140 ° C. The laminates composite were trimmed and cut to size to Tensile Test as per ASTM 03039- 76 and Impact Test as per ASTM 06110 for mechanical testing and surface analysis via Scanning Electron Microscope (SEM). Five samples of200mm x 15 mm x 3.5 mm were tested under tensile load at 2 mm I min. Five specimens were cut to dimension of 50 mm x 10 mm x 10 mm at angle+ 120 ° were tested under Impact Test. Surface analyses via SEM were made for specimens before and after mechanical testing. It was found that the average tensile stress at maximum load is 175.86 ± 4.49 MPa via UTM Instron. From Impact Test, the average energy absorbed is 27.5 J. SEM analysis of specimens after Impact Test showed that delaminataion, matrix cracking and fibre pull-out occur in the laminate composite systems. After tensile test, it was observed that brittle fracture occurs for the laminate composites with some fibre pull-out from composite system.

Item Type:Monograph (Project Report)
Uncontrolled Keywords:Composite materials -- Mechanical properties, Composite materials, Laminated materials -- Mechanical properties, Laminated materials
Subjects:T Technology > T Technology (General)
T Technology > TA Engineering (General). Civil engineering (General)
Divisions:Library > Projek Sarjana Muda > FKM
ID Code:8316
Deposited By:F Haslinda Harun
Deposited On:18 Jun 2013 18:46
Last Modified:23 Aug 2013 09:08

Repository Staff Only: item control page